Heat capacity of magnesium-neodymium hexaaluminate NdMgAl₁₁O₁₉

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Acesso é pago ou somente para assinantes

Resumo

Heat capacity of magnesium-neodymium hexaaluminate NdMgAl11O19 with the magnetoplumbite structure is measured by relaxation, adiabatic, and differential scanning calorimetry in the temperature range 2-1850 K. Smoothing of the data is carried out after matching the temperature dependences of the heat capacity obtained by different methods. Thermodynamic functions (entropy and enthalpy change) are calculated, and the anomalous Schottky heat capacity in the low temperature region is estimated.

Texto integral

Acesso é fechado

Sobre autores

P. Gagarin

N. S. Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Autor responsável pela correspondência
Email: gagarin@igic.ras.ru
Rússia, Moscow, 119991

A. Guskov

N. S. Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: gagarin@igic.ras.ru
Rússia, Moscow, 119991

V. Guskov

N. S. Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: gagarin@igic.ras.ru
Rússia, Moscow, 119991

M. Ryumin

N. S. Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: gagarin@igic.ras.ru
Rússia, Moscow, 119991

G. Nikiforova

N. S. Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: gagarin@igic.ras.ru
Rússia, Moscow, 119991

K. Gavrichev

N. S. Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: gagarin@igic.ras.ru
Rússia, Moscow, 119991

Bibliografia

  1. Lu H., Wang C.-A., Zhang C. // Ceram. Int. 2014. V. 40. P. 16273. https://doi.org/10.1016/j.ceramint.2014.07.064
  2. Chen X., Sun Y., Hu J., et al. // J. Europ. Ceram. Soc. 2020. V. 40. P. 1424. https://doi.org/10.1016/j.jeurceramsoc.2019.12.039
  3. Gadow R., Lischka M. // Surf. Coat. Tech. 2002. V. 151–152. P. 392. https://doi.org/10.1016/S0257-8972(01)01642-5
  4. Chen X., Gu L., Zou B., et al. // Surf. Coat. Tech. 2012. V. 206. P. 2265. doi: 10.1016/j.surfcoat.2011.09.076
  5. Gagarin P.G., Guskov A.V., Guskov V.N. et al. // Russ. J. Inorg. Chem. 2023. V. 68. P. 1460. https://doi.org/10.1134/S0036023623601861 [Гагарин П.Г., Гуськов А.В., Гуськов В.Н. и др. // Журн. неорган. химии. 2023. Т. 68. № 10. С. 1462.]
  6. Min X., Fang M., Huang Z. et al. // Opt. Mat. 2014. V. 37. P. 110. http://dx.doi.org/10.1016/j.optmat.2014.05.008
  7. Wang Y.-H., Ouyang J.-H., Liu Z.-G. // J. Alloys Comp. 2009. V. 485. P. 734. doi: 10.1016/j.jallcom.2009.06.068
  8. Lu H., Wang C.-A., Zhang C., et al. // J. Europ. Ceram. Soc. 2015. V. 35. P. 1297. http://dx.doi.org/10.1016/j.jeurceramsoc.2014.10.030
  9. Westrum E.F., Burriel R., Jr., Gruber J.B., et al. // J. Chem. Phys. 1989. V. 91. P. 4838. https://doi.org/10.1063/1.456722
  10. Tari A. The Specific Heat of Matter at Low Temperatures, Imperial College Press, 2003. 250 p.
  11. Gruber J.B., Justice B.H., Westrum E.F., Zandi B., Jr. // J. Chem. Thermodyn. 2002. V. 34. P. 457. doi: 10.1006/jcht.2001.0860
  12. Gruber J.B., Zandi B., Justice B.H., Westrum E.F., Jr. // J. Phys. and Chem. 2000. V. 61. P. 1189. https://doi.org/10.1021/j100726a052
  13. Bansal N.P., Zhu D. // Surf. Coat. Tech. 2008. V. 202. № 12. P. 2698. https://doi.org/10.1016/j.surfcoat.2007.09.048
  14. Shi Q., Snow C.L., Boerio-Goates J., Woodfield B.F. // J. Chem. Thermodyn. 2010. V. 42. P. 1107. doi: 10.1016/j.jct.2010.04.008
  15. Shi Q., Boerio-Goates J., Woodfield B.F. // J. Chem. Thermodyn. 2011. V. 43. P. 1263. doi: 10.1016/j.jct.2011.03.018
  16. Ryumin M.A., Nikiforova G.E., Tyurin A.V., et al. // Inorgan. Mater. 2020. V. 56. № 1. P. 97. doi: 10.1134/S0020168520010148 [Рюмин М.А., Никифорова Г.Е., Тюринидр А.В. // Неорган. материалы. 2020. Т. 56. № 1. С. 102. doi: 10.31857/S0002337X20010145]
  17. Малышев В.В., Мильнер Г.А., Соркин Е.Л., Шибакин В.Ф. // Приб. техн. эксп. 1985. Т. 6. С. 195.
  18. Furukawa G.T., McCoskey R.E., King G.J. // J. Res. Natl. Bur. Stand. 1951. V. 18. № 4. P. 256.
  19. Ditmars D.A., Ishihara S., Chang S.S., et al. // J. Res. Natl. Bur. Stand. 1982. V.87. № 2. P. 159. doi: 10.6028/jres.087.012
  20. Gagarin P.G., Guskov A.V., Guskov V.N. et al. // Rus. J. Inorg. Chem. 2023. V. 68. № 11. P. 1599. doi: 10.1134/S0036023623602064 [Гагарин П.Г., Гуськов А.В., Гуськов В.Н. и др. // Журн. неорган. химии. 2023. Т. 68. № 11. С. 1607. doi: 10.31857/S0044457X23601062]
  21. Prohaska T., Irrgeher J., Benefield J., et al. // Pure Appl. Chem. 2022. V. 94 (5). P. 573. https://doi.org/10.1515/pac-2019-0603
  22. Voskov A.L., Kutsenok I.B., Voronin G.F. // Calphad. 2018. V. 16. P. 50. https://doi.org/10.1016/j.calphad.2018.02.001
  23. Voronin G.F., Kutsenok I.B. // J. Chem. Eng. Data. 2013. V. 58. P. 2083. https://doi.org/10.1021/je400316m
  24. Восков А.Л. // Журн. физ. химии. 2022. Т. 96. № 9. С. 1296. doi: 10.31857/S0044453722090308 [Voskov A.L. // Russ. J. Phys. Chem. 2022. V. 96. P. 1895. https://doi.org/10.1134/S0036024422090291]
  25. Popa K., Jutier F., Wastin F., Konings R.J.M. // J. Chem. Thermodyn. 2006. V. 38. P. 1306–1311. doi: 10.1016/j.jct.2006.02.006
  26. Maier C.G., Kelley K.K.// J. Am. Chem. Soc. 1932. V 54. P. 3243–3246. doi: 10.1021/ja01347a029
  27. Kowalski P.M., Beridze G., Vinograd V.L., Bosbach D. // J. Nucl. Mater. 2015. V. 464. P. 147. https://doi.org/10.1016/j.jnucmat.2015.04.032
  28. Thiriet C., Konings R.J.M., Javorsky P., et al. // J. Chem. Thermodyn. 2005. V. 37. P. 131. doi: 10.1016/j.jct.2004.07.031

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar
2. Fig. 1. Diffraction pattern of neodymium magnesium hexaaluminate powder after annealing at 1700°C.

Baixar (100KB)
Metadados
3. Fig. 2. Type of temperature dependence of the heat capacity of NdMgAl₁₁O₁₉: ■ – relaxation calorimetry, ○ – adiabatic calorimetry, ▲ – differential scanning calorimetry.

Baixar (113KB)
Metadados
4. Fig. 3. Relative deviations of experimental values ​​of heat capacity of NdMgAl₁₁O₁₉ from smoothed values: ■ – relaxation calorimetry, ○ – adiabatic calorimetry, ▲ – differential scanning calorimetry.

Baixar (60KB)
Metadados
5. Fig. 4. Anomalous heat capacity of NdMgAl₁₁O₁₉: 1 – difference between the heat capacities of NdMgAl₁₁O₁₉ and LaMgAl11O19, 2 – excess heat capacity calculated for the energy levels of 71 cm⁻¹ and 250 cm⁻¹; vertical dashes show the 1% error corridor (a) and the anomalous heat capacity of NdMgAl₁₁O₁₉ in the temperature range of 2–20 K, calculated using equation (5) (b).

Baixar (142KB)
Metadados

Declaração de direitos autorais © Russian Academy of Sciences, 2025