Synthesis and Structure of Barium Hexaferrite BaFe12–xInxO19 (x = 0–1)

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

This study presents the results of the synthesis and examination of indium-substituted barium hexaferrite samples with the formula BaFe12–xInxO19. The ferrites were obtained via a solid state synthesis method. The substitution level of indium, represented by x(In), was varied from 0 to 1 in 0.25 increments. The stoichiometric formulas of the compounds were calculated using the EDS data. The powder X-ray diffraction analysis indicated that all samples form a single crystalline phase with the M-type hexaferrite structure. Parameters of the crystal unit cell were calculated from powder diffraction data. An expansion of the crystal lattice parameters was observed as iron was substituted with indium, from x = 0 to x = 0.84. The Curie temperatures of the synthesized ferrites were determined using differential scanning calorimetry (DSC) method. It is established that the Curie temperature decreases from 452 to 292°C with In content growth from x = 0 to x = 0.84 in the BaFe12–xInxO19.

全文:

受限制的访问

作者简介

A. Punda

South Ural State University (National Research University)

编辑信件的主要联系方式.
Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080

K. Gafarov

South Ural State University (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080

V. Zhivulin

South Ural State University (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080

A. Chernukha

South Ural State University (National Research University); Moscow Institute of Physics and Technology (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080; Dolgoprudny, 141701

A. Zykova

South Ural State University (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080

S. Gudkova

South Ural State University (National Research University); Moscow Institute of Physics and Technology (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080; Dolgoprudny, 141701

L. Pesin

South Ural State University (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080

G. Vyatkin

South Ural State University (National Research University)

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080

D. Vinnik

South Ural State University (National Research University); Moscow Institute of Physics and Technology (National Research University); St. Petersburg State University

Email: pundaai@susu.ru
俄罗斯联邦, Chelyabinsk, 454080; Dolgoprudny, 141701; St. Petersburg, 199034

参考

  1. Velhal N., Kulkarni G., Mahadik D., Chowdhury P., Barshilia H., Puri V. // J. Alloys Compd. 2016. Vol. 682. P. 730. doi: 10.1016/j.jallcom.2016.04.310
  2. Pullar R. // Progr. Mater. Sci. 2012. Vol. 57. P. 1191. doi: 10.1016/j.pmatsci.2012.04.001
  3. Xu Z., Qi Z., Wang G., Liu C., Cui J., Li W., Wang T. // Chinese Phys. (B). 2022. Vol. 33. N 3. doi: 10.1088/1674-1056/ac5240
  4. Tran N., Yang R., Jeong W., Manh D.H., Phan T., Lee B. // J. Am. Ceram. Soc. 2022. Vol. 105. P. 4122. doi: 10.1111/jace.18378
  5. Vovchenko L., Matzui L., Brusylovets L., Oliynyk V., Launets V., Shames A., Yakovenko O., Skoryk N. // Mater. Sci. Eng. Technol. 2016. Vol. 47. P. 139. doi: 10.1002/mawe.201600487
  6. Wang Y., Huang P., Tran N., Ayed H., Mouldi A. // Surfaces and Interfaces. 2022. Vol. 31. Art. no. 102065. doi: 10.1016/j.surfin.2022.102065
  7. Xiong X., Ma H., Mohammed J., Mehrez S., Alamri S., Giang H., Hoi H., // Ceram. Int. 2022. Vol. 48. P. 27420. doi: 10.1016/j.ceramint.2022.05.395
  8. Miranda F.A., Subramanyam G., Keuls F.W., Romanofsky R.R., Warner J.D., Mueller C.H. // IEEE Trans. Microwave Theory Technol. 2000. Vol. 48. P. 1181. doi: 10.1109/22.853458
  9. Suthar M., Roy P.K. // Mater. Sci. Eng. (B). 2022. Vol. 283. Art. no. 115801. doi: 10.1016/j.mseb.2022.115801
  10. Shakir H.M.F., Shahzad M., Aziz H.R., Rizwan M.S., Shahid S., Ali S.H., Zhao T. // J. Alloys Compd. 2022. Vol. 902. Art. no. 163847. doi: 10.1016/j.jallcom.2022.163847
  11. Hu Z., Koval V., Wu J., Yang B., Leavesley A., Wylde R., Reece M., Jia C., Yan H. // ACS App. Mater. Interfaces. 2022. Vol. 14. P. 46738. doi: 10.1021/acsami.2c13088
  12. Ahmed A., Prokhorov A.S., Anzin V., Bush A., Vinnik D. A., Gorshunov B., Alyabyeva L.N. // J. Alloys Compd. 2022. Vol. 898. P. 162761. doi: 10.1016/j.jallcom.2020.155462
  13. Alyabyeva L.N., Prokhorov A.S., Vinnik D.A., Anzin V.B., Ahmed A.G., Mikheykin A., Bednyakov P., Kadlec C., Kadlec F., Prado E., Prokleška J., Proschek P., Kamba S., Pronin A.V., Dressel M., Abalmasov V.A., Dremov V.V., Schmid S., Savinov M., Lunkenheimer P., Gorshunov B.P. // NPG Asia Mater. 2021. Vol. 13. Art. no. 63. doi: 10.1038/s41427-021-00331-x
  14. Gorbachev E.A., Trusov L.A., Sleptsova A.E., Kozlyakova E.S., Alyabyeva L.N., Yegiyan S.R., Prokhorov A.S., Lebedev V.A., Roslyakov I.V., Vasiliev A.V., Kazin P.E. // Mater. Today. 2020. Vol. 32. P. 13. doi: 10.1016/j.mattod.2019.05.020
  15. Song Y.Y., Ordóez-Romero Ć.L., Wu M. // Appl. Phys. Lett. 2009. Vol. 95. P. 142506. doi: 10.1063/1.3246170
  16. Harris V.G. // IEEE Trans. Magnetics. 2012. Vol. 48. P. 1075. doi: 10.1109/TMAG.2011.2180732
  17. Trukhanov A., Trukhanov S., Kostishyn V.G., Panina L.V., Salem M., Kazakevich I.S., Turchenko V., Kochervinsky V.V., Krivchenya D.A. // Phys. Solid State. 2017. Vol. 59. P. 737. doi: 10.1134/S1063783417040308
  18. Chen D., Liu Y., Li Y., Yang K., Zhang H. // J. Magn. Magn. Mater. 2013. Vol. 337–338. P. 65. doi 10.1016/ j.jmmm.2013.02.036
  19. Almessiere M.A., Slimani Y., Gungunes H., Ali S., Baykal A., Ercan I. // Ceram. Int. 2019. Vol. 45. N 8. P. 10048. doi: 10.1016/j.ceramint.2019.02.050
  20. Zhang W., Peng B., Zhang. W., Zhou S., Schmidt H. // J. Magn. Magn. Mater. 2010. Vol. 322. P. 1859. doi: 10.1016/j.jmmm.2009.12.041
  21. Песин Л.А., Гудкова С.А., Живулин В.Е., Павлова К.П., Стариков А.Ю., Шерстюк Д.П., Лебедев А.М., Чумаков Р.Г., Винник Д.А. // ЖСХ. 2023. Т. 64. Вып. 12. С. 119470. doi: 10.26902/JSC_id119470; Pesin L.A., Gudkova S.A., Zhivulin V.E., Pavlova K.P., Starikov A.Y., Sherstyuk D.P., Lebedev A.M., Chumakov R.G., Vinnik D.A. // J. Struct. Chem. 2023. Vol. 64. P. 2358. doi: 10.1134/S0022476623120077
  22. Wu C., Wang W., Li Q., Wei M., Luo Q., Fan Y., Jiang X., Lan Z., Jiao Z., Tian Y., Sun K., Yu. Z. // J. Am. Ceram. Soc. 2022. Vol. 105. P. 7492. doi: 10.1111/jace.18702
  23. Mahadevan S., Sankar A.R., Singh S., Sharma P. // J. Alloys Compd. 2023. Vol. 959. Art. no. 170456. doi: 10.1016/j.jallcom.2023.170456
  24. Li Y., Liu Q., Qi M., Chen Y. // J. Electr. Mater. 2023. Vol. 52. P. 523. doi: 10.1007/s11664-022-10021-1
  25. Mohammad F.Z., Huma F., Ali K. // J. Mater. Sci. 2023. Vol. 34. P. 1022. doi: 10.1007/s10854-023-10377-y
  26. Irshad Z., Bibi I., Ghafoor A., Majid F., Kamal S., Ezzine S., Elqahtani Z. M., Alwadai N., Messaoudi N., Iqbal M. // Res. Phys. 2022. Vol. 42. Art. no. 106006. doi: 10.1016/j.rinp.2022.106006
  27. Teh G.B., Nagalingam S., Jefferson D.A. // Mater. Chem. Phys. 2007. Vol. 101. P. 158. doi: 10.1016/j.matchemphys.2006.03.008
  28. Denisov V.M., Denisova L.T., Irtyugo L.A., Patrin G.S., Volkov N.V., Chumilina L.G. // Phys. Solid State. 2013. Vol. 55. P. 240. doi: 10.1134/S1063783412120116
  29. Zhang W., Li P., Wang Y., Guo J., Li J., Shan S., Ma S., Xing S. // Magnetochemistry. 2022. Vol. 8. P. 51. doi: 10.3390/magnetochemistry8050051
  30. Khan M.A., Afzal S., Gulbadan S., Mahmood K., Ashraf G.A., Akhtar M.N. // Ceram. Int. 2023. Vol. 49. P. 12144. doi: 10.1016/j.ceramint.2022.12.066
  31. Mohammed I., Mohammed J., Carol T.T., Srivastava A.K. // Hybrid Adv. 2023. Vol. 3. P. 100058. doi 10.1016/ j.hybadv.2023.100058
  32. Verma S., Singh A., Sharma S., Kaur P., Godara S.K., Malhi P.S., Ahmed J., Babu P.D., Singh M. // J. Alloys Compd. 2023. Vol. 930. P. 167410. doi: 10.1016/j.jallcom.2022.167410
  33. Manglam M.K., Kar M. // J. Alloys Compd. 2022. Vol. 899. Art. no. 163367. doi: 10.1016/j.jallcom.2021.163367
  34. Gorbachev E.A., Trusov L.A., Alyabyeva L.N., Roslyakov I.V., Lebedev V.A., Kozlyakova E.S., Magdysyuk O.V., Sobolev A.V., Glazkova I.S., Beloshapkin S.A., Gorshunov B.P., Kazin P.E. // Mater. Horizons. 2022. Vol. 9. P. 1264. doi: 10.1039/D1MH01797G
  35. Younus S., Murtaza G., Aloufi N.M., Somaily H.H. // Ceram. Int. 2022. Vol. 48. P. 31041. doi: 10.1016/j.ceramint.2022.07.065
  36. Agayev F., Trukhanov S., Trukhanov A., Jabarov S., Ayyubova G., Mirzayev M., Trukhanova E., Vinnik D., Kozlovskiy A., Zdorovets M., Sombra A., Zhou D., Jotania R., Singh C., Trukhanov A. // J. Therm. Anal. Calorim. 2022. Vol. 147. P. 14107. doi: 10.1007/s10973-022-11742-5
  37. Коровушкин В.В., Труханов А.В., Шипко М.Н., Костишин В.Г., Исаев И.М., Миронович А.Ю., Труханов С.В. // ЖНХ. 2019. T. 64. № 5. С. 463. doi: 10.1134/S0044457X19050118; Korovushkin V.V., Trukhanov A.V., Shipko M.N., Kostishin V.G., Isaev I.M., Mironovich A.Yu., Trukhanov S.V. // Russ. J. Inorg. Chem. 2019. Vol. 64. N 5. P. 574. doi: 10.1134/S0036023619050115
  38. Baykal A., Gungunes H., Sözeri H., Amir M., Auwal I., Asiri S., Shirsath S., Korkmaz A.D. // Ceram. Int. 2017. Vol. 43. N 17. P. 15486. doi: 10.1016/j.ceramint.2017.08.096
  39. Найден Е.П., Журавлев В.А., Минин Р.В., Итин В.И., Коровин Е.Ю. // Изв. вузов. Физика. 2015. Т. 58. Вып. 1. С. 112.
  40. Hong Y.S., Ho C.M., Hsu H.Y., Liu C.T. // J. Magn. Magn. Mater. 2004. Vol. 279. P. 401. doi 10.1016/ j.jmmm.2004.02.008
  41. Alange R., Khirade P., Birajdar S., Humbe A., Jadhav K.M. // J. Mol. Struct. 2015. Vol. 1106. P. 460. doi: 10.1016/j.molstruc.2015.11.004
  42. Lim E.S., Mun K.R., Kang Y.M. // J. Magn. Magn. Mater. 2018. Vol. 464. P. 26. doi: 10.1088/1757-899X/ 202/1/012040
  43. Hu S.L., Liu J., Yu H.Y., Liu Z.W. // J. Magn. Magn. Mater. 2019. Vol. 473. P. 79. doi: 10.1016/j.jmmm.2018.10.044
  44. Phan T.L., Tran N., Nguyen H.H., Yang D., Dang N., Lee B. // J. Alloys Compd. 2019. Vol. 216. Art. no. 152528. doi: 10.1016/j.jallcom.2019.152528
  45. Rianna M., Situmorang M., Kurniawan C., Tetuko A.P., Setiadi E.A., Ginting M., Sebayang P. // Mater. Lett. 2019. Vol. 256. Art. no. 126612. doi: 10.1016/j.matlet.2019.126612
  46. Rahman L., Rahman S., Biswas B. // Helion. 2023. Vol. 9. P. 1. doi: 10.1016/j.heliyon.2023.e14532
  47. Gordani G., Mohseni M., Ghasemi A., Hosseini S. // Mater. Res. Bull. 2016. Vol. 76. P. 187. doi: 10.1016/j.materresbull.2015.12.021
  48. Wong-Ng W., McMurdie H., Paretzkin B., Hubbard C., Dragoo A, // Powder Diffract. 1988. Vol. 3. P. 246.
  49. Shannon R.D. // Acta Crystallogr. 1976. Vol. 32. P. 751. doi: 10.1107/S0567739476001551

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Dependence of the indium content in the synthesized material on its content in the initial charge.

下载 (74KB)
索引源数据
3. Fig. 2. Diffractograms of BaFe12–xInxO19 solid solutions. The red bar chart indicates the literature data for BaFe12O19 [48].

下载 (176KB)
索引源数据
4. Fig. 3. Parameters of the elementary crystal cell of BaFe12–xInxO19. 1 – a (Å), 2 – c (Å), 3 – V (Å3) solid solutions.

下载 (109KB)
索引源数据
5. Fig. 4. Curie point values for solid solutions BaFe12–xInxO19 (error -2 °C).

下载 (60KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024