Copper(II) succinate: electrochemical synthesis, characterization and application as a precursor for micron-sized copper(II) oxide fibers

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

A coordination compound of copper(II) with succinic acid was obtained by electrochemical synthesis in media of various compositions. The samples were characterized by methods of quantitative analysis, ESR and IR spectroscopy, synchronous thermal analysis. The vibrational frequencies of copper(II) succinate were calculated by using DFT and the experimental IR spectra were interpreted on the basis of the results. Micro-sized copper(II) oxide fibers were obtained by thermal decomposition of synthesized samples. It was shown that the use of the water–dimethyl sulfoxide system with a volume ratio 1:1 is optimal to achieve the formation of moderately aggregated particles with a distinct filamentous morphology.

Толық мәтін

Рұқсат жабық

Авторлар туралы

E. Andriychenko

Kuban State University

Хат алмасуға жауапты Автор.
Email: leka91@mail.ru
ORCID iD: 0000-0002-2324-8987
Ресей, Krasnodar

V. Zelenov

Kuban State University

Email: leka91@mail.ru
ORCID iD: 0000-0003-3031-3844
Ресей, Krasnodar

A. Bespalov

Kuban State University

Email: leka91@mail.ru
ORCID iD: 0000-0002-9829-9674
Ресей, Krasnodar

V. Bovyka

Kuban State University

Email: leka91@mail.ru
ORCID iD: 0000-0001-9419-0818
Ресей, Krasnodar

Е. Panina

Kuban State University

Email: leka91@mail.ru
Ресей, Krasnodar

V. Volynkin

Kuban State University

Email: leka91@mail.ru
ORCID iD: 0000-0002-3352-9862
Ресей, Krasnodar

N. Bukov

Kuban State University

Email: leka91@mail.ru
ORCID iD: 0000-0001-8559-110X
Ресей, Krasnodar

Әдебиет тізімі

  1. Jia S., Wang Y., Liu X., Zhao S., Zhao W., Huang Y., Li Z., Lin Z. // Nano Energy. 2019. Vol. 59. P. 229. doi: 10.1016/j.nanoen.2019.01.081
  2. Wan M., Jin D., Feng R., Si L., Gao M., Yue L. // Inorg. Chem. Commun. 2011. Vol. 14. P. 38. doi 10.1016/ j.inoche.2010.09.025
  3. Yeoh J.S., Armer C.F., Lowe A. // Mater. Today Energy. 2018. Vol. 9. P. 198. doi: 10.1016/J.MTENER.2018.05.010
  4. Hameed M.U., Khan Y., Ali S., Wu Z., Dar S.U., Song H., Ahmad A., Chen Y. // Ceram. Int. 2017. Vol. 43. N 1(A). P. 741. doi: 10.1016/j.ceramint.2016.10.003
  5. Feng L., Xuan Zh., Bai Y., Zhao H., Li L., Chen Y., Yang X., Su Ch., Guo J., Chen X. // J. Alloys Compd. 2014. Vol. 600. P. 162. doi: 10.1016/j.jallcom.2014.02.132
  6. Anu Prathap M.U., Kaur B., Srivastava R. // J. Colloid Interface Sci. 2012. Vol. 370. P. 144. doi 10.1016/ j.jcis.2011.12.074
  7. Siddiqui H., Qureshi M.S., Haque F.Z. // Optik. 2016. Vol. 127. P. 2740. doi: 10.1016/j.ijleo.2015.11.220
  8. Rao M.P., Ponnusamy V.K., Wu J.J., Asiri A.M., Anandan S. // J. Environ. Chem. Eng. 2018. Vol. 6. P. 6059. doi: 10.1016/j.jece.2018.09.041
  9. Андрийченко Е.О., Зеленов В.И., Бовыка В.Е., Буков Н.Н. // ЖОХ. 2021. Т. 91. № 4. С. 638. doi: 10.31857/S0044460X2104020X; Andriychenko E.O., Zelenov V.I., Bovyka V.E., Bukov N.N. // Russ. J. Gen. Chem. 2021. Vol. 91. N 4. P. 707. doi: 10.1134/S1070363221040204
  10. Bhosale M.A., Karekar S.C., Bhanage B.M. // ChemistrySelect. 2016. Vol. 1. N 19. P. 6297. doi: 10.1002/slct.201601484
  11. Ganguly A., Ahmad T., Ganguli A.K. // Dalton Trans. 2009. Vol. 18. P. 3536. doi: 10.1039/B820778J
  12. Das S., Srivastava V.Ch. // Mater. Lett. 2015. Vol. 150. P. 130. doi: 10.1016/j.matlet.2015.03.018
  13. Rodríguez A., García-Vázquez J.A. // Coord. Chem. Rev. 2015. Vol. 303. P. 42. doi: 10.1016/j.ccr.2015.05.006
  14. Андрийченко Е.О., Зеленов В.И., Беспалов А.В., Бовыка В.Е., Буков Н.Н. // ЖОХ. 2021. Т. 91. № 9. С. 1416. doi: 10.31857/S0044460X21090134; Andriychenko E.O., Zelenov V.I., Bespalov A.V., Bovyka V.E., Bukov N.N. // Russ. J. Gen. Chem. 2021. Vol. 91. N 9. P. 1697. doi: 10.1134/S1070363221090139
  15. Cаргисян С.А., Саргсян Т.С., Агаджанян И.Г., Хизанцян К.М., Саркисян А.С., Маргарян К.С. // ЖОХ. 2020. Т. 90. Вып. 6. С. 906; Sargsyan S.H., Sargsyan T.S., Agadjanyan I.G., Khizantsyan K.M., Sargsyan A.S., Margaryan K.S. // Russ. J. Gen. Chem. 2020. Vol. 90. N 6. P. 906. doi: 10.31857/S0044460X20060108
  16. Ghoshal D., Ghosh A.K., Mostafa G., Ribas J., Chaudhuri N.R. // Inorg. Chim. Acta. 2007. Vol. 360. P. 1771. doi: 10.1016/j.ica.2006.08.054
  17. Kawata S., Kitagawa S., Machida H., Nakamoto T., Kondo M., Katada M., Kikuchi K., Ikemoto I. // Inorg. Chim. Acta. 1995. Vol. 229. P. 211. doi: 10.1016/0020-1693(94)04247-S
  18. Ghoshal D., Maji T.K., Mostafa G., Sain S., Lu T.-H., Ribas J., Zangrando E., Chaudhuri N.R. // Dalton Trans. 2004. Vol. 11. P. 1687. doi: 10.1039/b401738b
  19. Kawata S., Kitagawa S., Enomoto M., Kumagai H., Katada M. // Inorg. Chim. Acta. 1998. P. 80. doi: 10.1016/S0020-1693(98)00223-0
  20. González Garmendia M.J., San Nacianceno V., Seco J.M., Zúñiga F.J. // Acta Crystallogr. (C). 2009. Vol. 65. P. m436. doi: 10.1107/S0108270109040566
  21. O’Connor B.H., Maslen E.N. // Acta Crystallogr. 1966. Vol. 20. P. 824. doi: 10.1107/S0365110X66001932
  22. Rastsvetaeva R.K., Pushcharovsky D.Yu., Furmanova N.G. // Z. Kristallogr. Cryst. Mater. 1996. Vol. 211. P. 808. doi: 10.1524/zkri.1996.211.11.808
  23. Asai O., Kishita M., Kubo M. // J. Phys. Chem. 1959. Vol. 63. N 1. P. 96. doi: 10.1021/j150571a024
  24. Jasien P.G., Dhar S.K. // J. Inorg. Nucl. Chem. 1980. Vol. 42. N 6. P. 924. doi: 10.1016/0022-1902(80)80471-4
  25. Ganguly A., Ahmad T., Ganguli A.K. // Dalton Trans. 2009. P. 3536. doi: 10.1039/b820778j
  26. Djeghri A., Balegroune F., Guehria-Laidoudi A., Roisnel T. // Z. Kristallogr. NCS. 2004. Vol. 219. P. 471. doi: 10.1524/ncrs.2004.219.14.503
  27. Binitha M.P., Pradyumnan P.P. // Bull. Mater. Sci. 2017. Vol. 40. N 5. P. 1007. doi: 10.1007/s12034-017-1459-0
  28. Kozlevčar B., Leban I., Petrič M., Petriček S., Roubeau O., Reedijk J., Šegedin P. // Inorg. Chim. Acta. 2004. Vol. 357. P. 4220. doi: 10.1016/j.ica.2004.06.012
  29. Harish S.P., Sobhanadri J. // Inorg. Chim. Acta. 1985. Vol. 108. P. 147. doi: 10.1016/S0020-1693(00)84533-8
  30. Shee N.K., Verma R., Kumar D., Datta D. // Comput. Theor. Chem. 2015. Vol. 1061. P. 1. doi 10.1016/ j.comptc.2015.03.003
  31. Sharrock P., Melnik M. // J. Coord. Chem. 1985. Vol. 14. P. 65. doi: 10.1080/00958978508080679
  32. Andersson M.P., Uvdal P. // J. Phys. Chem. (A). 2005. Vol. 109. P. 2937. doi: 10.1021/jp045733a
  33. Nikumbh A.K., Pardeshi S.K., Raste M.N. // Thermochim. Acta. 2001. Vol. 374. P. 115. doi: 10.1016/S0040-6031(01)00483-X
  34. ГОСТ 10896-78. Иониты. Подготовка к испытанию. М.: ИПК Изд. стандартов, 1998. 7 с.
  35. Neese F. // WIREs Comput. Mol. Sci. 2012. Vol. 2. P. 73. doi: 10.1002/wcms.81
  36. Neese F. // WIREs Comput. Mol. Sci. 2017. Vol. 8:e1327. P. 1. doi: 10.1002/wcms.1327
  37. Becke A. D. // Phys. Rev. (A). 1988. Vol. 38. P. 3098. doi: 10.1103/PhysRevA.38.3098
  38. Lee C., Yang W., Parr R. G. // Phys. Rev. (B). 1988. Vol. 37. P. 785. doi: 10.1103/PhysRevB.37.785
  39. Grimme S., Ehrlich S., Goerigk L. // J. Comput. Chem. 2011. Vol. 32. P. 1456. doi: 10.1002/jcc.21759
  40. Allouche A.-R. // J. Comput. Chem. 2011. Vol. 32. P. 174. doi: 10.1002/jcc.21600

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig.1. EPR spectrum of a polycrystalline CuSuc–3 sample at 298 K.

Жүктеу (51KB)
Метадеректер
3. Fig.2. Optimized structure of a fragment of the copper(II) succinate polymer chain, calculation at the B3LYP-D3BJ/6-311G(d,p) level.

Жүктеу (128KB)
Метадеректер
4. Fig.3. TG–DSC curves for the CuSuc–3 sample.

Жүктеу (134KB)
Метадеректер
5. Fig.4. Electron microscopic images of fibers of the CuSuc–1 sample (a) and copper oxide obtained by its thermolysis at 400 (b) and 500°C (c).

Жүктеу (213KB)
Метадеректер
6. Fig.5. Electron microscopic images and histograms of the size distribution of copper(II) oxide microfibers: CuO–1 (a), CuO–2 (b), CuO–3 (c).

Жүктеу (449KB)
Метадеректер

© Russian Academy of Sciences, 2024